Metal fluoride compositions for self formed batteries

ABSTRACT

The described invention provides compositions related to an electronically insulating amorphous or nanocrystalline mixed ionic conductor composition comprising a metal fluoride composite to which an electrical potential is applied to form 1) a negative electrode, and 2) a positive electrode, wherein the negative electrode and positive electrode are formed in situ.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims benefit of priority to U.S. Application No.61/280,815, entitled “Metal fluoride compositions for self-formedbatteries,” filed Nov. 9, 2009, the content of which is incorporated byreference herein in its entirety.

STATEMENT OF GOVERNMENT FUNDING

This invention was made with government support. The government hascertain rights in the invention.

FIELD OF THE INVENTION

The described invention relates to primary and secondary electrochemicalenergy storage systems, particularly to such systems as battery cells,which use materials that take up and release ions as a means of storingand supplying electrical energy.

BACKGROUND

Electrochemical energy storage devices such as batteries are becomingincreasingly important to the rapid development of a wide variety oftechnologies ranging from small neural stimulators to electric vehicles.Addressing the power demands of these devices requires attention to avariety of performance factors. Although each application has adiffering set of priorities almost all have the same set of needs. Theseinclude greater gravimetric and volumetric energy density, lower cost,an increase in the ease of cell fabrication, and improved safety. Forthe past two decades, Li-ion technology has been the premiere batterytechnology and has evolved little since its first introduction. In thistechnology, both the positive and negative electrodes operate on thebasis of intercalation reactions where guest ions insert into a stablecrystalline host structure. For the positive electrode, this hoststructure typically has been layered (LiCoO₂) or three dimensional(LiMn₂O₄) host metal oxide structures. The positive electrode is theenergy limiting electrode of the Li-ion battery. Therefore attention tothe improvement of this electrode is key to the improvement of theenergy density of the battery. Existing and proposed intercalationmaterials are limited to the insertion of one lithium and one electronper formula unit; it is imperative for improved energy density that thislimitation is extended well beyond one electron and one ion. Recently aconcept of conversion materials has been introduced in order to set astage where two or three electrons can be transferred per transitionmetal thereby increasing the energy density of the battery by at least afactor of two (see Poizot, P, et al., Nature. 2000 Sep. 28;407(6803):496-9, the entire content of which is incorporated herein byreference). The most proficient conversion materials in this respecthave been the class of metal fluoride nanocomposites (see U.S. Ser. No.11/813,309; PCT/US06/00448; U.S. 60/727,471; U.S. 60/641,449; Bervas,M., et al., J. Electrochem. Soc. 2006. 153(4):A799-A808; Bervas, M., etal., Electrochem. Solid-State Lett. 2005. 8(4): A179-A183; Bervas, M.,et al., J. Electrochem. Soc. 2006. 153(1): A159-A170; Badway, F., etal., J. Electrochem. Soc. 2003. 150(10): A1318-A1327; Badway, F., etal., J. Electrochem. Soc. 2003. 150(9): A1209-A1218; Badway, F., et al.,Chem. Mater. 2007. 19:4129-4141; Pereira, N., J. Electrochem. Soc. 2009.156(6):A407-A416; Amatucci, G. G., and Pereira, N., J. Fluorine Chem.2007. 128:243-262; the contents of each of which are incorporated byreference herein in their entirety). During the discharge or lithiationreaction, the metal fluorides are reduced to the metal and LiF in asub-nanocomposite of dimensions <5 nm. The metal fluoride material isreformed during the subsequent charge or delithiation. This can beperformed many times over, thus affording rechargeability to thetechnology. The metal fluorides themselves are insulators, but suchappreciable electrochemical activity is made possible by the formationof nanocomposites, which enable the electrochemical activity of thematerials.

In many instances, a self formed battery based on fluoride electrodeswould be of interest and offers many important attributes. For example,without limitation, the use of a self formed battery would lower thefabrication cost considerably as there would not be any costs associatedwith individual electrode fabrication. Another example is that as anindefinite reserve battery, at the time of need, the cell would beformed into the highly reactive electrodes that normally would exhibitsome degradation if left in storage for long periods of time. Anotherexample is that the cell would be very easy to form into small orconformal dimensions as only one layer of fluoride material would haveto be deposited. As another example of high importance, the use of aself formed battery technology would enable the use of metal halideelectrodes of exceptional voltage and energy density but extremereactivity to the ambient environment and poor process stability.Forming such materials in-situ would eliminate the extreme difficulty ofhandling unstable materials, potential toxicity and especially high costof fabricating these materials ex-situ. In short the self-formedelectrochemical cell is utilized as a chemical factory itself. Anexample of the impact of this invention can be seen in the theoreticalenergy density of the successful incorporation of this concept to thein-situ formed Li/Ag—AgF₂ couple. This cell energy density would exceed3500 Wh/L, which is greater than 3× of today's state of the art Li-iontechnology.

The described invention relates to electrochemically formed metal halidebatteries and provides compositions and examples of a metal fluoridecell in which one of the components is a known glass former. In afurther embodiment, the battery may operate through a bi-ion energystorage mechanism where, upon the formation of the battery, a cation andanion, for example Li+ and F−, diffuse to opposing reactive currentcollectors to form the cell in situ.

SUMMARY

According to one aspect, the described invention provides anelectronically insulating amorphous or nanocrystalline mixed ionicconductor composition comprising a metal fluoride composite to which anelectrical potential is applied to form: a) a negative electrode; and b)a positive electrode; wherein the negative electrode and positiveelectrode are formed in situ. Additionally, the composition conductselectricity with ions as charge carriers. Additionally, the conductingions are cation(s) and anion(s). Additionally, the anion is a fluorideion. Additionally, the cation is an alkali metal. Additionally, thealkali metal is lithium. Additionally, the amorphous ion conductorcomposition further comprises a glass former. Additionally, the glassformer is a fluoride. Additionally, the glass former is selected fromthe group consisting of AlF₃, ZrF₄, GaF₃, HfF₄, YbF₃, ThF₃, ZnF₂, InF₃,ZbF₂, UF₃, and YF₃. Additionally, the amorphous ion conductorcomposition further comprises a fluoride glass network modifier.Additionally, the fluoride glass network modifier is a known fluorideconductor or contributes to fluoride conductivity. Additionally, theglass network modifier is selected from the group consisting of LaF₃,BiF₃, PbF₂, KF, CaF₂, BaF₂, SnF₂, SrF₂, or a rare earth metal fluoride.Additionally, the lithium further comprises a known lithium ionconductor. Additionally, the lithium is LiF. Additionally, the positiveelectrode is formed by a reaction with a positive current collector.Additionally, the positive reactive current collector comprises at leastone of Ag, Au, Bi, Pb, Sn, Cu, Pt, Pd, Fe, Mn, Ni, Mo, V or acombination thereof. Additionally, the positive reactive currentcollector comprises at least one of La, Ca, Ba, Sr, O, and S.Additionally, the positive current collector is comprised of carbon.Additionally, the carbon is a carbon selected from a carbon nanotube orgraphene. Additionally, the negative electrode is formed by a reactionwith a negative current collector. Additionally, the reactive negativecurrent collector comprises at least one of Ag, In, Al, Si, Sn, Ge, Mg,Au, Pd, Bi, Pb, graphite, carbon nanotubes, and graphene. Additionally,the conductor is formed as a compositionally graded material that allowspart of the composition to electrochemically oxidize to form thepositive electrode or to electrochemically reduce to form the negativeelectrode. Additionally, a nonaqueous liquid electrode is placed betweena negative reactive current collector and amorphous solid state bi-ionconducting electrolyte coated positive reactive current collector.Additionally, a nonaqueous liquid electrolyte is placed between apositive reactive current collector and a solid state bi-ion electrolytecoated negative reactive current collector.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A shows an illustrative interdigitated array (IDA) pattern withdigit width of approximately 250 micron with a spacing of approximately250 micron in a 8 mm×14 mm overall structure with a thickness ofapproximately 1 micron.

FIG. 1B shows XRD profiles of AlF₃/LiF/CaF₂ compositions fabricatedutilizing a LiF lithium conductor and various fluoride conducting glassnetwork modifiers.

FIG. 1C shows a schematic representation of the one embodiment of thedescribed invention that utilizes interpenetrating 3-D reactive positivecurrent collectors.

FIG. 2A shows a plot of current (mA) versus voltage of the amorphouscompositions AlF₃/LiF/CaF₂. FIG. 2B shows a schematic representation ofone embodiment of the described invention utilizing a bi-ion conductingamorphous coated reactive positive electrode and the incorporation of anon aqueous Li+ conducting electrolyte.

FIG. 3 shows a plot of voltage versus time representative of a dischargeprofile for a cell that has been charged at 5V constant current.

FIG. 4 shows XRD profiles of ZrF₄/LiF/CaF₂ compositions fabricatedutilizing a LiF lithium conductor and various fluoride conducting glassnetwork modifiers.

FIG. 5 shows a plot of current (mA) versus voltage comparing thepotentiodynamic response of the amorphous compositions ZrF₄/LiF/CaF₂,and one including BaF₂ as a substitute for CaF₂.

FIG. 6 shows a plot of voltage versus time (hour) illustrating arepresentative discharge profile for a cell that has been charged at 5Vconstant current.

FIG. 7 shows a plot of current (mA) versus cell voltage illustrating acomparison of the potentiodynamic response of compositions of 0.143MeF_(x)-0.428LiF-0.428CaF₂ where Me=Al, Hf, and Zr.

FIG. 8 shows a plot of current (mA) versus cell voltage illustrating acomparison of the potentiodynamic response of compositions of 0.143MeF_(x)-0.714LiF-0.143CaF₂ where Me=Al, Hf, and Zr.

FIG. 9 shows a schematic representative of the electrochemically formedcell.

FIG. 10 shows XRD profiles of deposited xZrF₄:(1-x)LiF films wherex=0.11, 0.14, and 0.2.

FIG. 11 shows a plot of voltage versus capacity (mAh) representing the10 nA discharge of the binary compositions (ZrF₄:LiF) after beingcharged for a very short 1 hour period at 5V.

FIG. 12 shows a plot of voltage versus capacity representing 200 nAformation charge as a function of Ca substitution in deposited Bi alloy.

FIG. 13 shows a plot of voltage versus capacity (mAh) representing 200nA formation charge as a function of Ag substitution in deposited Bialloy.

FIG. 14 shows a plot of voltage versus capacity (mAh) representing 200nA formation charge as a function of KF substitution in deposited Bialloy.

FIG. 15A shows a plot of voltage versus time (hour) of Bi negative/Bipositive current collector pairs utilizing amorphous LiF—ZrF₄composition of approximately 90:1 after sequentially longer periods ofcell formation. FIG. 15B shows a plot of voltage versus time (hour) ofAg negative/Ag positive current collector pairs utilizing amorphousLiF—ZrF₄ composition of approximately 90:1 after sequentially longerperiods of cell formation. FIG. 15C shows a plot of voltage versus time(hour) of Ag negative/Bi positive current collector pairs utilizingamorphous LiF—ZrF₄ composition of approximately 90:1 after sequentiallylonger periods of cell formation. FIG. 15D shows a plot of voltageversus time (hour) of Ti negative/Bi positive current collector pairsutilizing amorphous LiF—ZrF₄ composition of approximately 90:1 aftersequentially longer periods of cell formation.

FIG. 16 shows a plot of (i) charge capacity (mAh) versus time (hour) and(ii) discharge capacity (mAh) versus time (hour) of the Bi negative/Bipositive current collector pair utilizing amorphous LiF—ZrF₄ compositionof approximately 90:1 after sequentially longer periods of cellformation.

DETAILED DESCRIPTION

The described invention provides an electrochemically formed batterythat comprises at least two conducting ions, a cation and a fluorideanion, that react at opposing current collectors to form the negativeand positive electrodes of a battery, respectively, upon the formationof the battery. The described invention utilize a bi-ion conductingelectrolyte that can diffuse cations and fluoride anions.

The described invention further provides mixed ion conductors offluorides and an alkali metal in the nanocrystalline and amorphous statethat can be used to fabricate electrochemically self assembled batteriesof excellent reversibility and utilization. In some embodiments, thecompositions comprise an electrochemically stable glass former that canenhance fluoride conductivity such as, for example, ZrF₄, AlF₃, HfF₄,GaF₃, ScF₃, ThF₃, InF₃, and ZnF₂ (see Adam, J., J. Fluorine Chem. 2001.107:265-270; Poulain, M., Ann. Chim. Sci. Mat. 2003. 28:87-94;Trnovcová, V., et al. Ionics. 2001. 7:456-462; Sorokin, N. I., RussianChem. Rev. 2001. 9:801-807; Bobe, J. M., et al., J. Non-CrystallineSolids. 1997. 209:122-136; Dugat, P., et al. J. Solid State Chem. 1995.120:187-196; Ghosh, S., and Ghosh, A., Solid State Ionics. 2002.149:67-72; Savchuk, R. N., et al., 210^(th) Meeting of theElectrochemical Society, 2006 Joint International Meeting, Oct. 29-Nov.3, 2006. Cancun, Mexico, Abstract; Ghosh, S., and Ghosh, A., J. Phys.:Condens. Matter. 2005. 17:3463-3472; Savchuk, R. N., et al., 218^(th)ECS Meeting, Vol. 7, Issue 7, Oct. 10-Oct. 15, 2010, Las Vegas, Nev.,Abstract; Ghosh, S., and Ghosh, A., J. Appl. Physics, 2005. 97:123525;Ghosh, S., and Ghosh, A., J. Phys.: Condens. Matter, 2005. 17:3463-3472;and Sural, M., and Ghosh, A., Solid State Ionics, 1999. 120:27-32, thecontents of each of which are incorporated by reference herein in theirentirety). Alternatively, in some embodiments, the compositions comprisenon-fluoride glass formers, including those of borates and phosphates(see El-Hofy, M., and Hager, I. Z., phys. stat. sol. (a). 2003. 1999,No. 3, 448-456, the content of which is incorporated by reference hereinin its entirety), which support cation and/or anion conductivity.

Glossary

The term “amorphous” as used herein means not having long rangecrystalline structure, or a composite consisting of a nanostructuredphase (<100 nm) range and a phase with no order identifiable by x-raydiffraction.

The term “amorphous ion conductor” as used herein refers to a mediumwithout long range crystalline structure (as defined above) that allowsion conduction.

The term “anion” as used herein refers to a negatively charged ion.

The term “carbon nanotube” as used herein refers to an allotrope(meaning one of two or more different structural forms for an element)of carbon that has a cylindrical nanostructure.

The term “cation” as used herein refers to a positively charged ion.

In electrochemistry, the term “charge” is used to refer to the electriccharge (physical quantity) with positive or negative integer multiplesof the elementary electric charge, e. The sum of charges always isconserved within the time and space domains in which charge istransported. The term “charge” also frequently is used to refer to“positive charge” and “negative charge” just to indicate the sign of it.

The phrase “charge capacity of a battery” refers to the amount ofelectrical charge that is stored in a battery material and/or in anentire battery electrode. Charge capacity is measured in coulombs.Practically, charge is usually expressed in Ah (ampere hour). 1 Ah is3600 coulombs. Hence, the charge capacity of one mol of electroactivematerial that undergoes one electron transfer per process is 1 F or 26.8Ah. For the practical world of energy storage and conversion, highlyimportant is the specific charge (specific capacity), which is expressedin Ah per 1 gram (Ah g⁻¹) for gravimetric specific capacity or in Ah perliter (Ah L⁻¹) for volumetric capacity. It is important to distinguishbetween theoretical and practical specific capacity. “Theoreticalspecific charge capacity” is based on the molecular weight of the activematerial and the number of electron transfers in the electrochemicalprocess. “Practical specific charge capacity” is the actual capacitythat can be obtained in the process and it depends on many practicalfactors, such as the kinetic limitations of the electrochemical process,temperature of operation, cutoff voltage, electrodes design andconfiguration, and the like. In the fields of capacitors andrechargeable batteries, “charge capacity” defines the capacity that isinvolved in the charge process of the device, and is usually compared tothe capacity that is involved in the discharge process (“dischargecapacity”). The losses in the charge process should be minimal in orderfor good cycleability life of a device.

The term “coated” and its various grammatical forms as used hereinrefers to a thin outer layer or film applied to the surface of anobject.

The term “composite” as used herein refers to a compound comprising atleast one or more distinct components, constituents, or elements.

The term “conditional glass former” (intermediate) as used herein refersto a compound that does not assume the structure of a glass by itself,but that acts like a glass former when combined with anothercompound(s).

The term “conduction” as used herein refers to the flow of electricalcharge through a medium without the medium itself moving as a whole.

The term “conductive matrix” as used herein refers to a matrix thatincludes conductive materials, some of which may be ionic and/orelectronic conductors. Materials in which the matrix retains both ionicand electronic conductivity commonly are referred to as “mixedconductors.”

The term “conductivity” (or “electrical conductivity”, or “specificconductance”) as used herein refers to the ease with which an electriccurrent can flow through a body. Conductivity may be expressed assiemens per meter.

The term “conductor” (or “electric conductor”) as used herein refers toa medium which allows electric current to flow easily. Such a medium maybe, for example, a metal wire, a dissolved electrolyte, or an ionizedgas, among others.

The term “bi-ion conductor” as used herein refers to a solid statecomposition, which conducts cations and anions.

The term “crystal” refers to a homogenous solid formed by a repeating,three-dimensional pattern of atoms, ions, or molecules and having fixeddistances between constituent parts or the unit cell of such a pattern.The terms “crystal structure” or “crystal lattice” are usedinterchangeably herein to refer to the arrangement or formation of atomsor ions within the crystal.

The term “current” as used herein refers to the movement of electricalcharges in a conductor. The movement of electric charges carried byelectrons in an electronic conductor is referred to as an “electroniccurrent.” The movement of electrical charges carried by ions in an ionicconductor is referred to as “anionic current”.

The term “current collector” as used herein refers to that which gatherselectrons. Typically, a current collector is a structural part of anelectrode assembly. Its primary purpose is to conduct the electronsbetween the actual working (reacting) parts of the electrode and theterminals (the external electrical connection posts of anelectrochemical cell to which a power source or a load can beconnected). Current collector structures can be of interdigitated oropposing planar designs. Alternatively such structures may be of 3-Dincorporation within amorphous chemistry. In the invention describedherein, such current collectors can be reactive, meaning that upon cellformation, the current collectors react to form electrodes in situ.These are defined as “reactive current collectors.”

The term “electrical potential” (or “electric potential”) as used hereinrefers to the work required to bring a unit charge from a referencepoint to a specific point within an electric field. The reference pointusually is considered to be an infinite distance from the specificpoint, whose potential is considered to be zero. When 1 joule isrequired to bring 1 coulomb of charge, the potential is equal to 1 volt.

The term “electrolyte” as used herein refers to a compound thatdissociates into ions upon dissolution in solvents or/and upon melting,and which provides ionic conductivity. Compounds that possess a highionic conductivity in the solid state are called “solid electrolytes.”“True electrolytes” are those that are build up of ions in the solidstate (or pure form), whereas “potential electrolytes” are those thatform ions only upon dissolution and dissociation in solvents (i.e., theyexist as more or less covalent compounds in pure state).

The term “element” as used herein refers to simple substances whichcannot be resolved into simpler substances by normal chemical means.

The term “glass” as used herein refers to an extended, three-dimensionalnetwork of atoms that form a solid, which lacks the long-rangeperiodicity (or repeated, orderly arrangement) typical of crystallinematerials. Glasses lack the periodic (long range) order of a crystal,have infinite unit cell (no repeating large scale structures), acontinuous random network (a three-dimensional network lacking symmetryand periodicity), and are isotropic, having the same average packing andproperties in all directions. An “amorphous solid” has no long-rangeorder. In the context of this invention, the term “amorphous” or “glass”is understood to mean that the entire composition or portions of thecompositions on a nanometer or micron scale are without long range x-raydiffraction order.

The term “glassy” as used herein refers to structure that is nearlyX-ray amorphous with a crystalline structure in the nanometer range. Assuch, the term “glassy carbon” (vitreous carbon) refers to pure carbonthat combines glass-like mechanic characteristics with physicalproperties of graphite.

The term “glass former” as used herein refers to a compound that canreadily assume the structure of a glass or induce a glassy/amorphousstructure to compositions, which normally crystallize with long rangeorder. Generally, compounds with small cations form glasses whilecompounds with large, low valence cations do not form glasses. When anon-glass former is added to a glass former the continuous randomnetwork of the glass former is retained but that network has beenmodified by the addition of the non-glass former. These ionic compoundsare called “glass modifiers.”

The term “ion conductor” (or “ionic conductor”, or “IC”) as used hereinrefers to a material that conducts electricity with ions (meaning anelectrically charged chemical particle) as charge carriers (meaning theparticle carrying the electrical charge during the flow of electricalcurrent).

The term “ionic liquid” (or “liquid electrolytes”, “ionic metals”,“ionic fluids”, “fused salts”, “liquid salts”, or “ionic glasses”) asused herein refers to salts that form stable liquids. The term “ionicliquid” is inclusive of all classical molten salts, which are composedof more thermally stable ions.

The term “in situ” as used herein means in place or at a specific site.

The term “insulate” and its various grammatical forms as used hereinrefers to preventing the conduction of electrical, heat or sound energyinto or out of a material or body through the use of an insulator.

The term “insulator” (or “electrical insulator”) as used herein refersto a material that has sufficiently high resistance to the passage ofelectric current so that current flow through it is minimal ornegligible.

The term “metallic current collector” as used herein refers to a currentcollector made out of a metal.

The terms “micrometer” or “micron range” are used interchangeably hereinto refer to a dimension ranging from about 1 micrometer (10⁻⁶ m) toabout 1000 micrometers.

The term “mixed ionic conductor” as used herein refers to a conductorthat exhibits the mobility of at least two ions.

The term “molten” as used herein refers to a liquid state.

The term “nanocrystallite” as used herein refers to a discretecrystallite <100 nm in size or a crystallite <100 nm in sizeincorporated into a matrix resulting in the formation of ananocomposite. The final nanocomposite may or may not be of sizesgreater than 100 nm.

The terms “nanometer” or “nano range” are used interchangeably to referto a dimension ranging from about 1 nanometer (10⁻⁹ m) to about 1000nanometers.

The term “negative current collector” as used herein refers to a currentcollector that has gained electrons and has a net negative charge. Thenegative current collector may be a non reactive metal, such as Ti, Ni,Cu, Mo, Ca, La, Y, Li, or glassy carbon, or can be reactive in such thatit may form alloys or intermetallics with electrodeposited atoms suchas, but not limited to, Ag, In, Al, Si, Sn, Ge, Mg, Au, Pd, Bi, Pb,graphene, or a mixture of the above, or, in the case of carbon such as,but not limited to, graphite electrodes and carbon nanotubes, may resultin the formation of an intercalation compound. In addition, the alloyingmetal can be contained within the initial fluoride composition of theamorphous chemistry.

The term “positive current collector” as used herein refers to a currentcollector that has lost electrons and has a net positive charge.Reactive positive current collectors include those metals and compoundsthat can react with fluorine anions upon the charging of a cell to forma metal or carbon fluoride structure, but are not limited to, those ofsilver, bismuth, lead, tin, gold, copper, nickel, manganese, iron,cobalt, gold, palladium, and carbon (graphene, carbon nanotubes,graphite). Such current collectors can be formed as a mixed alloy, or ascomposites with each other or other elements to facilitate the chargetransport of the ions and electrons and subsequent formation of a metalor carbon fluoride within the electrode. Other components may be addedto the positive current collector, which do not react appreciably withfluoride anions during the charging process. This latter property may bedue to a non reactivity at the potentials imparted to the positiveelectrode, an intrinsic on reactivity at any voltage, or a kineticallyhindered non reactivity. As such, such elements will maintain their veryhigh electronic conductivity and enhance the electronic conductivity ofthe reactive positive electrode components.

The phrase “proximal to” as used herein means in direct contact orwithin 10 nm.

The term “reactive current collector” refers to the use of anelectronically conducting material that initially acts as a currentcollector, but later transforms in part or whole into an activeelectrode material by reaction with active ions upon the formation ofthe electrochemical cell.

The term “negative reactive current collector” as used herein refers toa reactive current collector that has gained electrons (been reduced)and has a net negative charge during the charge process of theelectrochemical cell.

The term “positive reactive current collector” as used herein refers toa reactive current collector that has lost electrons (been oxidized) andhas a net positive charge during the charge process of theelectrochemical cell.

The term “seed crystal” as used herein refers to a small piece of singlecrystal material from which a large crystal of the same materialtypically is to be grown. A liquid below its standard freezing pointwill crystallize in the presence of a seed crystal or nucleus aroundwhich a crystal structure can form (nucleation). However, lacking anysuch nucleus, the liquid phase can be maintained (supercooling).Supercooling is common in liquids that have difficulties forming initialseed crystals.

The phrase “solid state chemistry” (or “solid state forming chemistry”)as used herein refers to the study of the synthesis, structure, andphysical properties of solid materials.

The term “specific capacity” as used herein refers to the amount ofenergy a compound contains in milliamp hours (mAh) per unit weight. Theterm “reversible specific capacity” means that the compound may berecharged by passing a current through it in a direction opposite tothat of discharge.

The term “voltage” refers to the measure of the difference in electricpotential between two chosen points of space.

The term “watt” (“W”) refers to a unit of power. 1 W=1 J s⁻¹=1 V A.

I. Electronically Insulating Amorphous and Nanocrystalline Mixed IonicConductor Composition

According to one aspect, the described invention provides anelectronically insulating amorphous or nanocrystalline mixed ionicconductor composition comprising

(1) a metal fluoride composite to which an electrical potential isapplied to form

a) a negative electrode, and

b) a positive electrode,

wherein the negative electrode and positive electrode are formed insitu.

Additionally, the electronically insulating amorphous or nanocrystallinemixed ionic conductor composition conducts electricity with ions ascharge carriers.

Conducting Ions

Additionally, the conducting ion is a cation. Further, the cation is analkali metal. Alkali metals include, but are not limited to, lithium,sodium, potassium, rubidium, caesium, and francium.

Additionally, the amorphous or nanocrystalline mixed ionic conductorcomposition further comprises a lithium compound. Further, the lithiumcompound is a known lithium ion conductor. Further, the lithium compoundis LiF.

Additionally, the conducting ion is an anion. Further, the anion is afluoride ion.

Glass Formers

Additionally, the amorphous or nanocrystalline mixed ionic conductorfurther comprises a glass former. Further, the glass former is afluoride. Further, the glass former is ZrF₄. Further, the glass formeris AlF₃. Further, the glass former is HfF₃. Further, the glass former isScF₃. Further, the glass former is ThF₃. Further, the glass former isInF₃. Further, the glass former is ZbF₂. Further, the glass former isUF₃. Further, the glass former is YF₃. Further, the glass former isGaF₃. Further, the glass former is ZnF₂. Further, the glass former isInF₃.

Glass Network Modifier

Additionally, the amorphous or nanocrystalline mixed ion conductorfurther comprises a glass network modifier.

Additionally, the glass network modifier is a fluoride glass networkmodifier. Further, the fluoride glass network modifier is a knownfluoride conductor. Non limiting examples of such conductors includeLaF₃, BiF₃, PbF₂, CaF₂, BaF₂, SnF₂, SrF₂, or mixtures thereof, to formanion deficient compositions of exceptional conductivity. Further, thefluoride glass network modifier contributes to fluoride conductivity.Non limiting examples of such conductors include LaF₃, BiF₃, PbF₂, CaF₂,BaF₂, SnF₂, SrF₂, or mixtures thereof.

Further, the glass network modifier is CaF₂. Further, the glass networkmodifier is BaF₂. Further, the glass network modifier is SrF₂. Further,the glass network modifier is LaF₃. Further, the glass network modifieris a rare earth metal fluoride.

Further, the glass network modifier is LiF. Further, the glass networkmodifier is BiF₃. Further, the glass network modifier is PbF₂. Further,the glass network modifier is SnF₂. Further, the glass network modifieris SnF₄.

Electrode Formation

Additionally, the amorphous or nanocrystalline mixed ionic conductor isformed as a compositionally graded material, which allows part of thecomposition to electrochemically oxidize to form the positive electrodeor to electrochemically reduce to form the negative electrode.

Additionally, the amorphous or nanocrystalline mixed ionic conductor isformed as a composite.

Positive Electrode

Additionally, the composition comprises silver proximal to the positivecurrent collector. Additionally, the composition comprises bismuthproximal to the positive current collector. Additionally, thecomposition comprises palladium proximal to the positive currentcollector. Additionally, the composition comprises gold proximal to thepositive current collector. Additionally, the composition comprisescopper proximal to the positive current collector. Additionally, thecomposition comprises molybdenum proximal to the positive currentcollector.

Additionally, the positive electrode is formed by a reaction with areactive positive current collector. Further, the positive currentcollector comprises Ag. Further, the positive current collectorcomprises Au. Further, the positive current collector comprises Bi.Further, the positive current collector comprises Pb. Further, thepositive current collector comprises Sn. Further, the positive currentcollector comprises Cu. Further, the positive current collectorcomprises Pt. Further, the positive current collector comprises Pd.Further, the positive current collector comprises Mo. Further, thepositive current collector comprises V. Thus, primary componentsinclude, but are not limited to, Ag, Au, Bi, Pb, Sn, Cu, Pt, Pd, Mo, andV. Other elements that may aid in the F⁻ conductivity, but are notuseful as a positive electrode material due to low voltage and/orcapacity include, but are not limited to, K, Ca, La, Ba, Sr, and oxygen.

Additionally, the positive electrode is formed by a reaction with apositive current collector, wherein the positive current collectorcomprises at least one of Ag, Au, Bi, Pb, Sn, Cu, Pt, Pd, Mo, V, or acombination thereof. Thus, primary components include, but are notlimited to, Ag, Au, Bi, Pb, Sn, Cu, Pt, Pd, Mo, and V. Other elementsthat may aid in the F⁻ conductivity, but are not useful as a positiveelectrode material due to low voltage and/or capacity include, but arenot limited to, K, Ca, La, Ba, Sr, and oxygen.

Additionally, the positive electrode is formed by a reaction with apositive current collector, wherein the positive current collectorcomprises carbon. Further, the carbon is a carbon nanotube. Further, thecarbon is graphene. Further, the carbon is graphite.

Negative Electrode

Additionally, the negative electrode is formed by a reaction with anegative current collector.

Additionally, the negative current collector can be a non reactivemetal, such as Ti, Ni, Cu, Mo, Ca, La, Y, Li, or glassy carbon.Additionally, the negative current collector can be reactive in suchthat it may form alloys with the electrodeposited Li. Such materialsinclude Ag, In, Al, Si, Sn, Ge, Mg, Au, Pd, Bi, Pb, graphene, and thelike, or a mixture of any of the above, or may result in the formationof an intercalation compound in the case of carbon, such as graphiteelectrodes and carbon nanotubes.

Ionic Liquid

Additionally, the amorphous or nanocrystalline mixed ionic conductorcomprises an ionic liquid.

Additionally, a nonaqueous liquid electrolyte is placed between thenegative reactive current collector and the amorphous or nanocrystallineelectrolyte coated positive reactive current collector. Additionally, anonaqueous liquid electrolyte is placed between the positive reactivecurrent collector and the amorphous or nanocrystalline electrolytecoated negative reactive current collector. Further, nonaqueouselectrolytes include, but not are not limited to, a selection of lithiumsalts such as LiPF₆, LiBF₄, LiClO₄, LiF in various organic solventsincluding cyclic (propylene carbonate, ethylene carbonate) and acyclic(diethyl carbonate, dimethyl carbonate) carbonates, ethers, boranes(tris(pentafluorophenyl) borane) and nitriles (acetonitrile,methoxypropylnitrile, adiponitrile).

According to another aspect, the described invention provides anelectrochemical battery cell comprising:

(1) an electronically insulating amorphous or nanocrystalline mixedionic conductor composition comprising

(a) a metal fluoride composite to which an electrical potential isapplied to form

(i) a negative electrode, and

(ii) a positive electrode,

wherein the negative electrode and positive electrode are formed insitu.

Additionally, use of the described cells in ambient environments willrequire a near hermetic packaging around such cell. Such packaging iswell known to those who practice high energy batteries. Such packagingcan include multilayer metal polymer packaging, inorganic nano-layeredpackaging, packaging containing parylene, glass coatings, and the like.

Unless defined otherwise, all technical and scientific terms used hereinhave the same meaning as commonly understood by one of ordinary skill inthe art to which this invention belongs. Although any methods andmaterials similar or equivalent to those described herein can also beused in the practice or testing of the described invention, thepreferred methods and materials are now described. All publicationsmentioned herein are incorporated herein by reference to disclose anddescribe the methods and/or materials in connection with thepublications are cited.

It must also be noted that as used herein and in the appended claims,the singular forms “a,” “and” and “the” include plural referents unlessthe context clearly dictates otherwise. All technical and scientificterms used herein have the same meaning

The publications discussed herein are provided solely for theirdisclosure prior to the filing date of the present application. Nothingherein is to be construed as an admission that the described inventionis not entitled to antedate such publication by virtue of priorinvention. Further, the dates of publication provided may be differentfrom the actual publication dates which may need to be independentlyconfirmed.

It should be understood by those skilled in the art that various changesmay be made and equivalents may be substituted without departing fromthe true spirit and scope of the Invention. In addition, manymodifications may be made to adapt a particular situation, material,composition of matter, process, process step or steps, to the objective,spirit and scope of the described invention. All such modifications areintended to be within the scope of the claims appended hereto.

EXAMPLES

The following examples are put forth so as to provide those of ordinaryskill in the art with a complete disclosure and description of how tomake and use the present invention, and are not intended to limit thescope of what the inventors regard as their invention nor are theyintended to represent that the experiments below are all or the onlyexperiments performed. Efforts have been made to ensure accuracy withrespect to numbers used (e.g. amounts, temperature, etc.) but someexperimental errors and deviations should be accounted for. Unlessindicated otherwise, parts are parts by weight, molecular weight isweight average molecular weight, temperature is in degrees Centigrade,and pressure is at or near atmospheric.

Example 1 Amorphous Compositions

A variety of primarily amorphous compositions of fluoride andfluoride/Li conductors were fabricated as per Table 1 as examples of thetype of compositions useful for the described invention. “Mixtures”refer to the thickness of the sample compositions. “Ag” is utilized asthe reactive positive and negative electrode, “Ti” indicates thethickness of the adhesion aid of the Ti deposited between the glasssubstrate and the Ag interdigitation.

TABLE 1 EXAMPLE OF COMPOSITIONS FABRICATED Sample composition (Molarratios) Mixtures (nm) Ti (nm) Ag (nm) AIF₃-Li (1:1) 1100 11 500 AIF₃-LiF(1:1) 1000 10 500 AIF₃-LiFLaF₃ (1:2:2) 1000 — 500 AIF₃-LiF (1:4) 1000 50500 AIF₃-LiF (1:6) 1000 40 500 AIF₃-LiF:CaF₂ (1:2:2) 966 42 500 YbF₃-LiF(1:4) 1080 42 500 AIF₃-LiF-CaF₂ (1:1:3) 1015 60 510 AIF₃-LiF CaF₂(1:3:1) 1002 58.5 501 AIF₃-LiF CaF₂ (1:3:3) 1006 30 500 ZrF₄-LiF-CaF₂(1:2:2) 1006 30 500 AIF₃-LiF-CaF₂ (1:5:1) 1151 58.5 501 AIF₃-LiF CaF₂(1:3:3) 1001 36 1000 AIF₃-LiF CaF₂ (1:3:3) 1001 40 500 AIF₃-LiF CaF₂(.75:3:3) 1001 40 500 AIF₃-LiF CaF₂ (1:5:3) 1008 50 500 AIF₃-LiF CaF₂(1:5:1) 1002 50 500 ZrF₄-LiF-CaF₂ (1:5:1) 1038 50 501 HfF₄-LiF-CaF₂(1:2:2) 835 50 501 HfF₄-LiF-CaF₂ (1:3:3) 610 7 500 B₂O₃-LiF-CaF₂ (1:5:1)1010 50 501 ZrF₄-LiF-BaF₂ (1:3:3) 1010 50 500 ZrF₄-LiF-BaF₂ (1:5:1) 101050 501

All compositions contained a percentage (%) of a glass former. In thisexample a range of fluoride glass formers were utilized including AlF₃,ZrF₄, GaF₃, HfF₄, YbF₃. Although these glass formers were utilized,other known fluoride glass formers can be utilized, including, but notlimited to ThF₃, InF₃, ZbF₂, UF₃, YF₃ etc. A glass former with a highelectrolytic stability and ability to form electronically insulatingglasses can be utilized, as well as those glass formers that wouldcontribute to the fluoride anion conductivity.

The glass formers were combined with glass modifiers, which are also Fconductors. These include LiF, CaF₂, BaF₂, and LaF₃. Other modifierswhich exhibit considerable F conduction can be utilized such as BiF₃,PbF₂, SnF₂, SnF₄.

Finally LiF was added as a Li source for electrochemically formedbatteries of this invention that rely on Lithium and fluoride diffusion.

Forming a material composition of the aforementioned materials mostideally would result in a dual ion conducting system exhibiting at leastfast Li⁺ and F ionic conductivity.

The represented compositions were mixed well with a mortar and pestleand deposited as thin films onto an interdigitated current collectorstructure through the use of thermal evaporation.

Sensitivity to current collector material selection is needed as suchcurrent collectors can combine with the mobile species to result in anelectrochemically formed electrode (i.e. reactive current collectors).For example, the positive current collector most ideally would form avery high energy density electrode with the F⁻ ion. Therefore thereactive current collector should be of a material composition to do so.Positive current collectors of silver, bismuth, lead, tin, gold, iron,nickel, palladium, copper, carbon (carbon nanotubes, graphene, graphite)all can be considered viable current collector materials that willanodically form representative metal or carbon fluorides with the mobileF−—ion and a subsequent positive electrode of exceptionally high energydensity. Such current collectors can be formed as a mixed alloy, ascomposites, or as compositionally graded structures to facilitate thecharge transport of the ions and electrons to easily form the desiredmetal fluoride. For example, a small amount of bismuth, lead, orlanthanum, can be added to form bismuth fluoride based compounds withina matrix of silver to enable fast diffusion of fluoride ion deep withinthe structure. In addition, to aid in the transfer of electrons to theexternal circuit of the battery, the positive current collector cancontain (in the form of a micron or nanoscaled composite) anelectronically percolating network of a metal that does not react withF− in appreciable amounts. For example, gold, platinum, or non reactivecarbons may be added to guarantee fast electron transfer between theactive material and the external structure of the battery.

The negative current collector can be a non reactive metal, such as Ti,Ni, Cu, Mo, Ca, La, Y, Li, glassy carbon, or can be reactive, such thatit can form alloys with the electrodeposited Ag, In, Al, Si, Sn, Ge, Mg,Au, Pd, Bi, Pb, graphene, etc., or a mixture of any of the above, or canresult in the formation of an intercalation compound in the case ofcarbon such as graphite electrodes and carbon nanotubes. In addition,the alloying metal can be contained with the initial bi-ion conductingfluoride composition. For example, during formation, Al from AlF₃ coulddeposit near the negative current collector, and then subsequently alloywith the electrochemically reduced Li to form a Li_(x)Al alloy. Reactivecurrent collector structures can be of interdigitated or opposing planardesigns. Alternatively such structures may be of three dimensionalincorporation within the amorphous chemistry. In order to facilitateintimate and high surface interface with the self forming fluoridechemistry, it would be advantageous to have the current collector of amicro or nano morphology such that interpenetrating contact between themetal current collector and the bi-ion conducting fluoride chemistry canoccur (see FIGS. 1A and 1C). Therefore the current collector structurescould be columnar or structured in other morphologies to afford suchintimate contact. Such structures may be on the order of microns ornanometers.

For most of the examples demonstrated herein, the current collectorswere fabricated of 500 nm Ag in an interdigitated design (see, forexample, Table 1 (column 4) and FIGS. 1A and 1C).

Although thermal evaporation was utilized to deposit the amorphousfluoride compositions, other physical vapor deposition methods, such aselectron beam evaporation, sputtering techniques, plasma deposition, andchemical vapor deposition techniques can be utilized to fabricate thefilms. In addition, low cost techniques which can extend the conceptbeyond thin film to structures of 10s to 100s of microns of thicknesscan be utilized, such as sol gel chemistry with spin or dip coating, arcmelting and quenching, and even traditional melt—quench or melt-castprocesses that have been utilized by those familiar with the state ofthe art in glass manufacturing.

All the electrochemical tests below were fabricated by thermalevaporation of the reactive current collectors in an interdigitatedarray (IDA) pattern with digit width of approximately 250 micron with aspacing of approximately 250 micron in a 8 mm×14 mm overall structure,as shown in FIG. 1A, with a thickness of approximately 1 micron. FIG. 1Cshows a schematic representation of the one embodiment of the describedinvention that utilizes interpenetrating 3-D reactive positive currentcollectors. The amorphous compositions were deposited on top of theinterdigitated array at a thickness of approximately 1 micron. Allelectrochemical tests were performed inside an argon filled glovebox toeliminate impact of ambient atmosphere. It is understood by thosefamiliar with the art of nonaqueous battery technologies that quasihermetic encapsulation can be applied to enable performance of thebattery in an ambient environment.

Example 2 Glass Compositions Consisting of AlF₃ Glass Former

As per Table 1, various compositions containing AlF₃ as the glass formerwere investigated for their physical and electrochemical properties.FIG. 1B shows plots of intensity (a.u.) versus degrees (2-theta)representing the XRD profiles of AlF₃/LiF/CaF₂ compositions fabricatedutilizing a LiF lithium conductor and various fluoride conducting glassnetwork modifiers. As can be seen, all samples are very amorphous with aslight Bragg reflection with 2θ values between 47 and 48 degrees relatedto a nanophase of CaF₂ for CaF₂ rich compositions. FIG. 2A shows a plotof current (mA) versus cell voltage of the amorphous compositionsAlF₃/LiF/CaF₂ illustrating potentiodynamic sweeps of the amorphouscompositions. As can be seen in FIG. 2A, the first charge evolvesconsiderable anodic current relating to the formation of the battery.The subsequent discharge shows significant cathodic current in thevoltage region of 2-4V. This is consistent with a formed Li—Agalloy/solid state electrolyte/AgF_(x) based battery. Subsequent cyclesshow that the cycling stability of the compositions is excellent. Anincreasing electrochemical utility is seen for the compositionscontaining greater amounts of LiF. FIG. 3 shows a plot of voltage versustime representative of a discharge profile for one such cell that hasbeen charged at 5V constant current. As can be seen, considerablecapacity is evolved from the battery at useful voltages.

Example 3 Glass Compositions of ZrF₄ Glass Former

As per Table 1, various compositions containing ZrF₄ as the glass formerwere investigated for their physical and electrochemical propertiesafter being deposited on top of reactive current collectors for both thepositive and negative electrodes. FIG. 4 shows plots of intensity (a.u.)versus degrees (2-theta) representing XRD profiles of ZrF4/LiF/CaF2compositions fabricated utilizing a LiF lithium conductor and variousfluoride conducting glass network modifiers. As can be seen, all samplesare very amorphous with only a slight Bragg reflection with 2θ valuesbetween 46 and 48 degrees related to a nanophase of CaF₂ for the samplewith the greatest quantity of CaF₂ in the composition. FIG. 5 shows aplot of current (mA) versus voltage comparing the potentiodynamicresponse of the amorphous compositions ZrF₄/LiF/CaF₂, and one includingBaF₂ as a substitute for CaF₂. As can be seen in FIG. 5, the firstcharge evolves considerable anodic current relating to the formation ofthe battery. The subsequent discharge shows significant cathodic currentin the voltage region of 2-4V. This is consistent with a formed Li—Agalloy/solid state electrolyte/AgF_(x) based battery. As with the AlF₃study of Example 2, those compositions with highest LiF contentexhibited the greatest electrochemical utility. The potentiodynamicsweeps of FIG. 5 also show that the BaF₂ modified fluoride compositiondemonstrated considerable electrochemical utility. Subsequent cyclesshows that the cycling stability of the compositions is excellent.

FIG. 6 shows a plot of voltage versus time (hour) illustrating arepresentative discharge profile for such a cell that has been chargedat 5V constant voltage then discharged at a constant current of 10 nA.Considerable capacity is evolved from the battery at useful voltages.

Example 4 Comparison of Various Glass Formers

FIG. 7 shows a plot of current (mA) versus cell voltage illustrating acomparison of the potentiodynamic response of compositions of 0.143MeF_(x)-0.428LiF-0.428CaF₂ where Me=Al, Hf, and Zr. All threecompositions resulted in an amorphous film. All three films resulted inappreciable electrochemical activity and good reversibility after beingdeposited on top of reactive current collectors for both the positiveand negative electrodes. FIG. 8 shows a plot of current (mA) versus cellvoltage illustrating a comparison of the potentiodynamic response ofcompositions of 0.143 MeF_(x)-0.714 LiF-0.143 CaF₂ where Me=Al, Hf, andZr. The best electrochemical utility for the three examples was observedfor the compositions utilizing the AlF₃ glass former. However if the LiFcomposition is raised to 0.143 MeF_(x)-0.714 LiF-0.143 CaF₂, FIG. 8shows that the best electrochemical utility is observed for the ZrF₄glass former.

Without being bound by theory, it is believed that ZrF₄ compositionsgave the best performance because such compositions exhibit the fastestdual ion conductivity in the form of Li⁺ and F⁻. Without being bound bytheory, it is believed that compositions which exhibit fasterconductivities will give even more improved performance as long as thecompositions are stable towards the electrochemical decomposition of thenetwork former. Such compositions may extend to the fluoroborates andfluorophoshates as these compositions should exhibit goodelectrochemical stability.

Bi-ion conducting compositions unstable to the applied electrochemicalpotential also can be utilized. Within such a concept, the glass formeror modifier can be oxidized or reduced to become part of the positive ornegative electrode, respectively. For example, AlF₃ glass former mayreduce at the negative electrode to form Al, which will then act as analloying agent for lithium upon full cell formation. In suchapplications, it may be preferable to have a gradient in compositions ofthe amorphous fluoride between the positive to the negative electrode.FIG. 2B shows a schematic representation of one embodiment of thedescribed invention utilizing a bi-ion conducting amorphous coatedreactive positive electrode and the incorporation of a non aqueous Li+conducting electrolyte. In this embodiment, a nonaqueous liquidelectrolyte is placed between the negative reactive current collectorand the amorphous bi-ion conducting electrolyte coated positive reactivecurrent collector (see FIG. 2B). Additionally, a nonaqueous liquidelectrolyte is placed between the positive reactive current collectorand the amorphous bi-ion electrolyte coated negative reactive currentcollector. Nonaqueous electrolytes include, but not are not limited to,a selection of lithium salts such as LiPF₆, LiBF₄, LiClO₄, LiF invarious organic solvents including cyclic (propylene carbonate, ethylenecarbonate) and acyclic (diethyl carbonate, dimethyl carbonate)carbonates, ethers, boranes (tris(pentafluorophenyl) borane) andnitriles (acetonitrile, methoxypropylnitrile, adiponitrile). Further,fluoride compositions exhibiting the dual ion conductivity requirementfor such a self formed cell also can be in the form of molten fluoridesalts (ionic liquids).

Example 5 Example of Binary LiF Containing Compositions

FIG. 9 shows a schematic representative of one embodiment of theelectrochemically formed cell. A binary composition of LiF:ZrF₄ isplaced between two silver reactive current collectors. The cell then iselectrically polarized to induce the Li⁺ ion diffusion towards thenegative reactive current collector, at which the Li⁺ ion reduces toform a Li_(x)Ag alloy. In a parallel reaction, the F−—ion diffusestowards the positive electrode to form silver fluorides through anoxidation reaction. Afterwards, the cell can be discharged toreestablish the starting components.

FIG. 10 shows a plot of intensity (a.u.) versus 2-theta representing theXRD patterns of deposited xZrF₄:(1-x)LiF films where x=0.11, 0.14, and0.2. Even though a very small amount of ZrF₄ glass former is present,the films deposit as amorphous compositions. FIG. 11 shows a plot ofcell voltage versus capacity (mAh) representing the 10 nA discharge ofthe binary compositions (ZrF₄:LiF) after being charged for a very short1 hour period at 5V. It can be seen from the discharge profiles in FIG.11 that the samples with the greatest amount of LiF had the highestelectrochemical activity.

For the examples below, unless otherwise noted, the typicalcharge/formation protocol of the in-situ formed cell was 200 nA to 4.75Vfollowed by a constant voltage hold at 4.75V until the current decayedto approximately 10 nA. This is followed by a discharge of variouscurrents using 10 nA as the minimum current. All examples below utilizean amorphous bi-ion conductor composition consisting of 90 LiF 10 ZrF₄,which was deposited as a 1 micron film on top of the followinginterdigitated arrays. All cell structures were of the aforementionedinterdigitated cell as represented by the schematic illustration ofFIGS. 1A and 1C. Unless otherwise indicated, the negative digit was Bimetal of approximate thickness of 500 nm. The same thickness wasutilized for the positive electrode.

Example 6 Example of Positive Electrode Metallization Composites: Bi+Ca

The Bi—Ca alloy positive reactive current collector was deposited invarious ratios as depicted in Table 2 below:

TABLE 2 Alloy μAh Charge @ 200n A μAh Discharge 0Ca:1Bi (0:100) 0.2 41Ca:8Bi (12.5:87.5) 8 x 1.5Ca:8Bi (18.8:81.2) 12 11 1Ca:3Bi (25:75) 2426

FIG. 12 shows a plot of voltage versus capacity (mAh) representing 200nA formation charge as a function of Ca substitution in deposited Bialloy; the Bi—Ca alloy positive reactive current collector was depositedin various ratios as depicted in Table 2. The data show that significantimprovement in the constant current voltage profile and resultingformation capacity and the following discharge capacity can be realizedwith proper amounts of Ca additions. This shows that the use of aheterogeneous reactive current collector can be advantageous. While notbeing bound by theory, the in situ formed electrode may be a calciumsubstituted bismuth fluoride, which would have improved F− diffusion.

Example 7 Example of Positive Electrode Metallization Composites: Bi+Ag

The Bi—Ag alloy positive reactive current collector was deposited invarious ratios as depicted in Table 3.

TABLE 3 Alloy μAh @ 200 nA Charge μAh Discharge 0Ag:1Bi (0Ag:100Bi) 0.24 1Ag:8Bi (12.5:87.5Bi) 17.5 30 1Ag:3Bi (25Ag:75Bi) 22 4 1Ag:1Bi(50Ag:50Bi) 7 3 3Ag:1Bi (75Ag:25Bi) 1 1

FIG. 13 shows a plot of voltage versus capacity (mAh) representing 200nA formation charge as a function of Ag substitution in deposited Bialloy; the Bi—Ag alloy positive reactive current collector was depositedin various ratios as depicted in Table 3. The data show that significantimprovement in the constant current voltage profile, resulting formationcapacity, and the following discharge capacity can be realized withproper amounts of Ag additions. This shows that the use of aheterogeneous reactive current collector can be advantageous. Withoutbeing bound by theory, the in situ formed electrode may result in asilver substituted bismuth fluoride which would have improved Fdiffusion. In addition, the highly conductive silver may act as a fasttransport pathway for the electrons to diffuse from the reaction zoneduring the formation and subsequent charge reactions.

Example 8 Example of Positive Electrode Metal+Nonmetal Composites: Bi+KF

The Bi—KF alloy positive reactive current collector was deposited invarious ratios as depicted in Table 4.

TABLE 4 Alloy μAh Charge @ 200 nA μAh Discharge 0KF:1Bi (0KF:100Bi) 0.24 1KF:8Bi (12.5KF:87.5Bi) 11 7

87.5 Bi along with 12.5 KF mixed positive reactive current collectorswere fabricated. FIG. 14 shows a plot of voltage versus capacity (mAh)representing 200 nA formation charge as a function of KF substitution indeposited Bi alloy; the Bi—KF alloy positive reactive current collectorwas deposited in various ratios as depicted in Table 4. The data showsignificant improvement in the constant current voltage profile andresulting formation capacity and the following discharge capacity can berealized with addition of KF (see FIG. 14). This shows that the use of ametal/inorganic compound composite can be beneficial to theelectrochemical activity of the invention.

Example 9 Example of Various Negative and Positive ElectrodeMetallization Composites

Various negative/positive current collector pairs were deposited in athickness of 500 nm to demonstrate the flexibility and influence of thechosen chemistries on the resulting electrochemical properties of thedescribed invention. The cells were charged/formed at 5V forsequentially longer periods of time and discharged at 10 nA after eachperiod. The resulting discharge curves are shown in FIG. 15. FIG. 15Ashows a plot of voltage versus time (hour) of Bi negative/Bi positivecurrent collector pairs utilizing amorphous LiF—ZrF₄ composition ofapproximately 90:1 after sequentially longer periods of cell formation.FIG. 15B shows a plot of voltage versus time (hour) of Ag negative/Agpositive current collector pairs utilizing amorphous LiF—ZrF₄composition of approximately 90:1 after sequentially longer periods ofcell formation. FIG. 15C shows a plot of voltage versus time (hour) ofAg negative/Bi positive current collector pairs utilizing amorphousLiF—ZrF₄ composition of approximately 90:1 after sequentially longerperiods of cell formation. FIG. 15D shows a plot of voltage versus time(hour) of Ti negative/Bi positive current collector pairs utilizingamorphous LiF—ZrF₄ composition of approximately 90:1 after sequentiallylonger periods of cell formation. As can be seen from these data, thechoice of current collector couple has a distinct impact on the averagevoltage and electrochemical utilization of the cell. The use of both Agand Ti negative current collectors was found to result in highervoltages than that of Bi. Without being bound by theory, this isconsistent with the expected voltages of plated Li on Ti, Li—Ag alloy,and Li—Bi in the post formed cell.

FIG. 16, which is an accounting of the accumulated charge and dischargecapacities for the Bi/Bi couple of FIG. 15, shows a plot of (i) chargecapacity (mAh) versus time (hour) and (ii) discharge capacity (mAh)versus time (hour) of the Bi negative/Bi positive current collector pairutilizing amorphous LiF—ZrF₄ composition of approximately 90:1 aftersequentially longer periods of cell formation. An excellent agreementbetween the accumulated charge and discharge capacity can be seen foreach cycle, showing that this invention displays excellent reversibilityand efficient utilization of the charge current during the subsequentdischarge.

While the described invention has been described with reference to thespecific embodiments thereof, it should be understood by those skilledin the art that various changes may be made and equivalents may besubstituted without departing from the true spirit and scope of theinvention. In addition, many modifications may be made to adapt aparticular situation, material, composition of matter, process, processstep or steps, to the objective, spirit and scope of the describedinvention. All such modifications are intended to be within the scope ofthe claims appended hereto.

1. An electronically insulating amorphous or nanocrystalline mixed ionicconductor composition comprising a metal fluoride composite to which anelectrical potential is applied to form: a) a negative electrode; and b)a positive electrode; wherein the negative electrode and positiveelectrode are formed in situ.
 2. The composition according to claim 1,wherein composition conducts electricity with ions as charge carriers.3. The composition according to claim 2, wherein the conducting ions arecation(s) and anion(s).
 4. The composition according to claim 3, whereinthe anion is a fluoride ion.
 5. The composition according to claim 3,wherein the cation is an alkali metal.
 6. The composition according toclaim 5, wherein the alkali metal is lithium.
 7. The compositionaccording to any one of claims 1-4, wherein the amorphous ion conductorcomposition further comprises a glass former.
 8. The compositionaccording to claim 7, wherein the glass former is a fluoride.
 9. Thecomposition according to claim 7, wherein the glass former is selectedfrom the group consisting of AlF₃, ZrF₄, GaF₃, HfF₄, YbF₃, ThF₃, ZnF₂,InF₃, ZbF₂, UF₃, and YF₃.
 10. The composition according to any one ofclaims 1-4, wherein the amorphous ion conductor composition furthercomprises a fluoride glass network modifier.
 11. The compositionaccording to claim 10, wherein the fluoride glass network modifier is aknown fluoride conductor or contributes to fluoride conductivity. 12.The composition according to claim 10, wherein the glass networkmodifier is selected from the group consisting of LaF₃, BiF₃, PbF₂, KF,CaF₂, BaF₂, SnF₂, SrF₂, or a rare earth metal fluoride.
 13. Thecomposition according to claim 6, wherein the lithium further comprisesa known lithium ion conductor.
 14. The composition according to claim 6,wherein the lithium is LiF.
 15. The composition according to claim 1,wherein the positive electrode is formed by a reaction with a positivecurrent collector.
 16. The composition according to claim 15, whereinthe positive reactive current collector comprises at least one of Ag,Au, Bi, Pb, Sn, Cu, Pt, Pd, Fe, Mn, Ni, Mo, V or a combination thereof.17. The composition according to claim 16, wherein the positive reactivecurrent collector comprises at least one of La, Ca, Ba, Sr, O, and S.18. The composition according to claim 15, wherein the positive currentcollector is comprised of carbon.
 19. The composition according to claim18, wherein the carbon is a carbon selected from a carbon nanotube orgraphene.
 20. The composition according to claim 1, wherein the negativeelectrode is formed by a reaction with a negative current collector. 21.The composition according to claim 20, wherein the reactive negativecurrent collector comprises at least one of Ag, In, Al, Si, Sn, Ge, Mg,Au, Pd, Bi, Pb, graphite, carbon nanotubes, and graphene.
 22. Thecomposition according to claim 1, wherein the conductor is formed as acompositionally graded material that allows part of the composition toelectrochemically oxidize to form the positive electrode or toelectrochemically reduce to form the negative electrode.
 23. Thecomposition according to claim 22, wherein a nonaqueous liquid electrodeis placed between a negative reactive current collector and an amorphoussolid state bi-ion conducting electrolyte coated positive reactivecurrent collector.
 24. The composition according to claim 22, wherein anonaqueous liquid electrolyte is placed between a positive reactivecurrent collector and a solid state bi-ion electrolyte coated negativereactive current collector.